This study demonstrates the hybridization of Li4Ti5O12 (LTO) with different types of carbon onions synthesized from nanodiamonds. The carbon onions mixed with a Li4Ti5Ox precursor for sol–gel synthesis. These hybrid materials are tested as anodes for both lithium-ion battery (LIB) and sodium-ion battery (SIB). Electrochemical characterization for LIB application is carried out using 1 m LiPF6 in a 1:1 (by volume) ethylene carbonate and dimethyl carbonate as the electrolyte. For lithium-ion intercalation, LTO hybridized with carbon onions from the inert-gas route achieves an excellent electrochemical performance of 188 mAh g−1 at 10 mA g−1, which maintains 100 mAh g−1 at 1 A g−1 and has a cycling stability of 96% of initial capacity after 400 cycles, thereby outperforming both neat LTO and LTO with onions obtained via vacuum treatment. The performance of the best-performing hybrid material (LTO with carbon onions from argon annealing) in an SIB is tested, using 1 m NaClO4 in ethylene/dimethyl/fluoroethylene carbonate (19:19:2 by mass) as the electrolyte. A maximum capacity of 102 mAh g−1 for the SIB system is obtained, with a capacity retention of 96% after 500 cycles.
We present a versatile strategy to tailor the nanostructure of monolithic carbon aerogels. By use of an aqueous colloidal solution of polystyrene in the sol-gel processing of resorcinol-formaldehyde gels, we can prepare, after supercritical drying and successive carbonization, freestanding monolithic carbon aerogels, solely composed of interconnected and uniformly sized hollow spheres, which we name carbon spherogels. Each sphere is enclosed by a microporous carbon wall whose thickness can be adjusted by the polystyrene concentration, which affects the pore texture as well as the mechanical properties of the aerogel monolith. In this study, we used monodisperse polystyrene spheres of approximately 250 nm diameter, which result in an inner diameter of the final hollow carbon spheres of approximately 200 ± 5 nm due to shrinkage during the carbonization process. The excellent homogeneity of the samples, as well as uniform sphere geometries, are confirmed by small- and angle X-ray scattering. The presence of macropores between the hollow spheres creates a monolithic network with the benefit of being reversibly compressible up to 10% linear strain without destruction. Electrochemical tests demonstrate the applicability of ground and CO2 activated carbon spherogels as electrode materials.