This work introduces the facile and scalable two-step synthesis of Ti 2 Nb 10 O 29 (TNO)/carbon hybrid material as a promising anode for lithium-ion batteries (LIBs). The first step uses a mechanically-induced self-sustaining reaction via ball-milling at room temperature to produce titanium niobium carbide with a stoichiometric ratio of Ti and Nb of 1 to 5. The second step involves the oxidation of as-synthesized titanium niobium carbide to produce TNO. Synthetic air yields fully oxidized TNO, while annealing in CO 2 results in TNO/carbon hybrids. The electrochemical performance for the hybrid and non-hybrid electrodes was surveyed for a narrow potential window (1.0-2.5 V vs. Li/Li + ) and a large potential window (0.05-2.5 V vs. Li/Li + ). The best hybrid material displayed a specific capacity of 350 mAh/g at a rate of 0.01 A/g (144 mAh/g at 1 A/g) in the large potential window regime. The electrochemical performance of hybrid materials is superior compared to non-hybrid materials for operation within the large potential window. Due to the advantage of carbon in hybrid material, the rate handling is faster than that of the non-hybrid one. The hybrid materials display robust cycling stability and maintain ca. 70% of their initial capacities after 500 cycles. In contrast, only ca. 26% of the initial capacity is maintained after the first 40 cycles for non-hybrid materials. We also applied our hybrid material as an anode in a full-cell lithium-ion battery by coupling it with commercial LiMn 2 O 4 .
This study presents electrospun niobium carbide/carbon (NbC/C) hybrid nanofibers, with an average diameter of 69 +/- 30 nm, as a facile precursor to derive either highly nanoporous niobium carbide-derived carbon (NbC-CDC) fibers for supercapacitor applications or niobium pentoxide/carbon (Nb2O5/C) hybrid fibers for battery-like energy storage. In all cases, the electrodes consist of binder-free and free-standing nanofiber mats that can be used without further conductive additives. Chlorine gas treatment conformally transforms NbC nanofiber mats into NbC-CDC fibers with a specific surface area of 1508 m2 g-1. These nanofibers show a maximum specific energy of 19.5 W h kg-1 at low power and 7.6 W h kg-1 at a high specific power of 30 kW kg-1 in an organic electrolyte. CO2 treatment transforms NbC into T-Nb2O5/C hybrid nanofiber mats that provide a maximum capacity of 156 mA h g-1. The presence of graphitic carbon in the hybrid nanofibers enabled high power handling, maintaining 50% of the initial energy storage capacity at a high rate of 10 A g-1 (64 C-rate). When benchmarked for an asymmetric full-cell, a maximum specific energy of 86 W h kg-1 was obtained. The high specific power for both systems, NbC-CDC and T-Nb2O5/C, resulted from the excellent charge propagation in the continuous nanofiber network and the high graphitization of the carbon structure.
Performance stability in capacitive deionization (CDI) is particularly challenging in systems with a high amount of dissolved oxygen due to rapid oxidation of the carbon anode and peroxide formation. For example, carbon electrodes show a fast performance decay, leading to just 15% of the initial performance after 50 CDI cycles in oxygenated saline solution (5 mM NaCl). We present a novel strategy to overcome this severe limitation by employing nanocarbon particles hybridized with sol-gel-derived titania. In our proof-of-concept study, we demonstrate very stable performance in low molar saline electrolyte (5 mM NaCl) with saturated oxygen for the carbon/metal oxide hybrid (90% of the initial salt adsorption capacity after 100 cycles). The electrochemical analysis using a rotating disk electrode (RDE) confirms the oxygen reduction reaction (ORR) catalytic effect of FW200/TiO2, preventing local peroxide formation by locally modifying the oxygen reduction reaction.
MXene as a novel intercalation-type pseudocapacitive cathode and anode for capacitive deionization
(2016)
In this proof-of-concept study, we introduce and demonstrate MXene as a novel type of intercalation electrode for desalination via capacitive deionization (CDI). Traditional CDI cells employ nanoporous carbon electrodes with significant pore volume to achieve a large desalination capacity via ion electrosorption. By contrast, MXene stores charge by ion intercalation between the sheets of its two-dimensional nanolamellar structure. By this virtue, it behaves as an ideal pseudocapacitor, that is, showing capacitive electric response while intercalating both anions and cations. We synthesized Ti3C2-MXene by the conventional process of etching ternary titanium aluminum carbide i.e., the MAX phase (Ti3AlC2) with hydrofluoric acid. The MXene material was cast directly onto the porous separator of the CDI cell without added binder, and exhibited very stable performance over 30 CDI cycles with an average salt adsorption capacity of 13 +/- 2 mg g-1.